Influence of pH and temperature of dip-coating solution on the properties of cellulose acetate-ceramic composite membrane for ultrafiltration.

Polymer-ceramic composite membranes were prepared by dip coating technique using 5?wt.% cellulose acetate (CA) solution at different temperatures (15?°C, 25?°C and 40?°C). The effect of pH (2-12) of the polymeric solution on the properties of the membranes was studied using SEM, EDAX, FTIR, gas and liquid permeation. The thickness of the polymeric layer depended on the interaction of CA solution with the surface of ceramic support. Membrane permeability decreased with increase in pH because of decrease in pore size and porosity resulting from strong interaction of the polymer layer with the ceramic support. The porosity and mean pore size of the prepared membranes were found to be 28-60% and 30-47?nm (ultrafiltration range), respectively. The optimized membrane (pH 7) was used for ultrafiltration of oil in water emulsions (100 and 200?mg/L). Oil rejection of 99.61% was obtained for 100?mg/L of oil concentration in water.