Deterioration of the mechanical properties of calcium phosphate cements with Poly (?-glutamic acid) and its strontium salt after in vitro degradation.

Title Deterioration of the mechanical properties of calcium phosphate cements with Poly (?-glutamic acid) and its strontium salt after in vitro degradation.
Authors T. Liang; C.X. Gao; L. Yang; H.L. Yang; Z.P. Luo
Journal J Mech Behav Biomed Mater
DOI 10.1016/j.jmbbm.2017.07.026
Abstract

The mechanical reliability of calcium phosphate cements has restricted their clinical application in load-bearing locations. Although their mechanical strength can be improved using a variety of strategies, their fatigue properties are still unclear, especially after degradation. The evolutions of uniaxial compressive properties and the fatigue behavior of calcium phosphate cements incorporating poly (?-glutamic acid) and its strontium salt after different in vitro degradation times were investigated in the present study. Compressive strength decreased from the 61.2±5.4MPa of the original specimen, to 51.1±4.4, 42.2±3.8, 36.8±2.4 and 28.9±3.2MPa following degradation for one, two, three and four weeks, respectively. Fatigue life under same loading condition also decreased with increasing degradation time. The original specimens remained intact for one million cycles (run-out) under a maximum stress of 30MPa. After degradation for one to four weeks, the specimens were able to withstand maximum stress of 20, 15, 10 and 10MPa, respectively until run-out. Defect volume fraction within the specimens increased from 0.19±0.021% of the original specimen to 0.60±0.19%, 1.09±0.04%, 2.68±0.64% and 7.18±0.34% at degradation time of one, two, three and four weeks, respectively. Therefore, we can infer that the primary cause of the deterioration of the mechanical properties was an increasing in micro defects induced by degradation, which promoted crack initiation and propagation, accelerating the final mechanical failure of the bone cement. This study provided the data required for enhancing the mechanical reliability of the calcium phosphate cements after different degradation times, which will be significant for the modification of load-bearing biodegradable bone cements to match clinical application.

Citation T. Liang; C.X. Gao; L. Yang; H.L. Yang; Z.P. Luo.Deterioration of the mechanical properties of calcium phosphate cements with Poly (?-glutamic acid) and its strontium salt after in vitro degradation.. J Mech Behav Biomed Mater. 2017;75:190196. doi:10.1016/j.jmbbm.2017.07.026

Related Elements

Phosphorus

Phosphorus Bohr ModelSee more Phosphorus products. Phosphorus (atomic symbol: P, atomic number: 15) is a Block P, Group 15, Period 3 element. The number of electrons in each of Phosphorus's shells is 2, 8, 5 and its electronic configuration is [Ne] 3s2 3p3. The phosphorus atom has a radius of 110.5.pm and its Van der Waals radius is 180.pm. Phosphorus is a highly-reactive non-metallic element (sometimes considered a metalloid) with two primary allotropes, white phosphorus and red phosphorus its black flaky appearance is similar to graphitic carbon. Compound forms of phosphorus include phosphates and phosphides. Phosphorous was first recognized as an element by Hennig Brand in 1669 its name (phosphorus mirabilis, or "bearer of light") was inspired from the brilliant glow emitted by its distillation.

Calcium

See more Calcium products. Calcium (atomic symbol: Ca, atomic number: 20) is a Block S, Group 2, Period 4 element with an atomic weight of 40.078. The number of electrons in each of Calcium's shells is [2, 8, 8, 2] and its electron configuration is [Ar]4s2. Calcium Bohr ModelThe calcium atom has a radius of 197 pm and a Van der Waals radius of 231 pm. Calcium was discovered and first isolated by Sir Humphrey Davy in 1808. It is the fifth most abundant element in the earth's crust and can be found in minerals such as dolomite, gypsum, plagioclases, amphiboles, pyroxenes and garnets. In its elemental form, calcium has a dull gray-silver appearance. Calcium is a reactive, soft metal that is a member of the alkaline earth elements. Elemental CalciumIt frequently serves as an alloying agent for other metals like aluminum and beryllium, and industrial materials like cement and mortar are composed of calcium compounds like calcium carbonate. It is also an biologically essential substance found in teeth, bones, and shells. The name "calcium" originates from the Latin word "calics," meaning lime.

Strontium

See more Strontium products. Strontium (atomic symbol: Sr, atomic number: 38) is a Block S, Group 2, Period 5 element with an atomic weight of 87.62 . Strontium Bohr ModelThe number of electrons in each of Strontium's shells is [2, 8, 18, 8, 2] and its electron configuration is [Kr] 5s2. The strontium atom has a radius of 215 pm and a Van der Waals radius of 249 pm. Strontium was discovered by William Cruickshank in 1787 and first isolated by Humphry Davy in 1808. In its elemental form, strontium is a soft, silvery white metallic solid that quickly turns yellow when exposed to air. Elemental StrontiumCathode ray tubes in televisions are made of strontium, which are becoming increasingly displaced by other display technologies pyrotechnics and fireworks employ strontium salts to achieve a bright red color. Radioactive isotopes of strontium have been used in radioisotope thermoelectric generators (RTGs) and for certain cancer treatments. In nature, most strontium is found in celestite (as strontium sulfate) and strontianite (as strontium carbonate). Strontium was named after the Scottish town where it was discovered.

Related Forms & Applications